Technology
Chemical composition and mechanical property under annealed condition ferritic stainless steels
| Brand | Chemical components % | Mechanical property under annealed condition | ||||||||||||
|
C≤ |
Si≤ |
Mn≤ |
P≤ |
S≤ |
Cr |
Mo |
Cu |
N |
Ohter | Yield strength MPa ≥ |
Tension strength MPa ≥ |
Elongation % ≥ |
Hardness HV ≤ |
|
|
SUS429 |
0.12 |
1.00 |
1.00 |
0.040 |
0.030 |
14.00-16.00 |
--- |
--- |
--- |
--- |
205 |
450 |
22 |
200 |
|
SUS430 |
0.12 |
0.75 |
1.00 |
0.040 |
0.030 |
16.00-18.00 |
--- |
--- |
--- |
--- |
205 |
450 |
22 |
200 |
|
SUS430LX |
0.030 |
0.75 |
1.00 |
0.040 |
0.030 |
16.00-19.00 |
--- |
--- |
--- |
Ti 或 Nb 0.00～1.00 |
175 |
360 |
22 |
200 |
|
SUS430J1L |
0.025 |
1.00 |
1.00 |
0.040 |
0.030 |
16.00-20.00 |
--- |
--- |
0.025 |
Ti，Nb，ZrOr a combination thereof8×(C%+N%)～0.80Cu 0.30～0.80 |
205 |
390 |
22 |
200 |
|
SUS436L |
0.025 |
1.00 |
1.00 |
0.040 |
0.030 |
16.00-19.00 |
0.75-1.50 |
--- |
0.025 |
Ti，Nb，Zr Or a combination thereof8×(C%+N%)～0.80 |
245 |
410 |
20 |
230 |
|
SUS444 |
0.025 |
1.00 |
1.00 |
0.040 |
0.030 |
17.00-20.00 |
1.75-2.50 |
--- |
0.025 |
Ti，Nb，Zr Or a combination thereof8×(C%+N%)～0.80 |
245 |
410 |
20 |
230 |